PROGRESSIVE FRACTURE MODELING OF THE FAILURE WAVE IN IMPACTED GLASS

The failure wave has been observed propagating in glass under impact loading since1991. It is a continuous fracture zone which may be associated with the damage accumulation process during the propagation of shock waves. A progressive fracture model was proposed to describe the failure wave formation and propagation in shocked glass considering its heterogeneous meso-structures. The original and nucleated microcracks will expand along the pores and other defects with concomitant dilation when shock loading is below the Hugoniot Elastic Limit. The governing equation of the failure wave is characterized by inelastic bulk strain with material damage and fracture. And the inelastic bulk strain consists of dilatant strain from nucleation and expansion of microcracks and condensed strain from the collapse of the original pores. Numerical simulation of the free surface velocity was performed and found in good agreement with planar impact experiments on K9 glass at China Academy of Engineering Physics. And the longitudinal,lateral and shear stress histories upon the arrival of the failure wave were predicted, which present the diminished shear strength and lost spall strength in the failed layer.

作 者： Yao Guowen Liu Zhanfang Huang Peiyan   作者單位： Yao Guowen(College of Civil Engineering and Architecture, Chongqing Jiaotong University, Chongqing 400074, China)

Liu Zhanfang(Department of Engineering Mechanics, Chongqing University, Chongqing 400044, China)

Huang Peiyan(College of Traffic and Communications, South China University of Technology, Guangzhou 510640, China) 

刊 名： 固體力學學報（英文版）  SCI 英文刊名： ACTA MECHANICA SOLIDA SINICA  年，卷(期)： 2006 19(1)  分類號： O34  關(guān)鍵詞： the failure wave   progressive fracture model   glass   planar impact  

【PROGRESSIVE FRACTURE MODELING OF THE】相關(guān)文章：

Progress in modeling of fluid flows in crystal growth processes04-26

A kinetic modeling study of pollutant formation in premixed hydrocarbon flames04-25

Automated Separation of Stars and Normal Galaxies Based on Statistical Mixture Modeling with RBF Neural Net-works04-27